Nuclear graphite is any grade of graphite, usually synthetic graphite, manufactured for use as a moderator or reflector within a nuclear reactor. Graphite is an important material for the construction of both historical and modern nuclear reactors because of its extreme purity and ability to withstand extremely high temperatures.
History
[edit]Nuclear fission, the creation of a nuclear chain reaction in uranium, was discovered in 1939 following experiments by Otto Hahn and Fritz Strassman, and the interpretation of their results by physicists such as Lise Meitner and Otto Frisch.[1][2] Shortly thereafter, word of the discovery spread throughout the international physics community.
In order for the fission process to chain react, the neutrons created by uranium fission must be slowed down by interacting with a neutron moderator (an element with a low atomic weight, that will "bounce", when hit by a neutron) before they will be captured by other uranium atoms. By late 1939, it was generally known that heavy water might be used as a moderator. Graphite was dismissed by the Germans as a possible moderator because it contained boron as an impurity. However, graphite of high enough purity was developed in the early 1940's in the United States, and this then was utilized in the first and subsequent nuclear reactors for the Manhattan Project. [3]
In February 1940, using funds that were allocated partly as a result of the Einstein-Szilard letter to President Roosevelt, Leo Szilard purchased several tons of graphite from the Speer Carbon Company and from the National Carbon Company (the National Carbon Division of the Union Carbide and Carbon Corporation in Cleveland, Ohio) for use in Enrico Fermi's first fission experiments, the so-called exponential pile.[4]: 190 Fermi writes that "The results of this experiment was [sic] somewhat discouraging"[5] presumably because of the absorption of neutrons by some unknown impurity.[6]: 40 So, in December 1940 Fermi and Szilard met with Herbert G. MacPherson and V. C. Hamister at National Carbon to discuss the possible existence of impurities in graphite.[7]: 143 During this conversation it became clear that minute quantities of boron impurities were the source of the problem.[3][8]
As a result of this meeting, over the next two years, MacPherson and Hamister developed thermal and gas extraction purification techniques at National Carbon for the production of boron-free graphite.[8][9] The resulting product was designated AGOT Graphite ("Acheson Graphite Ordinary Temperature") by National Carbon, and it was "the first true nuclear grade graphite".[10]
During this period, Fermi and Szilard purchased graphite from several manufacturers with various degrees of neutron absorption cross section: AGX graphite from National Carbon Company with 6.68 mb (millibarns) cross section, US graphite from United States Graphite Company with 6.38 mb cross section, Speer graphite from the Speer Carbon Company with 5.51 mb cross section, and when it became available, AGOT graphite from National Carbon, with 4.97 mb cross section.[6]: 178 [11]: 4 [12] By November 1942 National Carbon had shipped 250 tons of AGOT graphite to the University of Chicago[4]: 200 where it became the primary source of graphite to be used in the construction of Fermi's Chicago Pile-1, the first nuclear reactor to generate a sustained chain reaction (December 2, 1942).[6]: 295 In early 1943 AGOT graphite was used to build the X-10 Graphite Reactor at Clinton Engineer Works in Tennessee and the first reactors at the Hanford Site in Washington,[11]: 5 for the production of plutonium during and after World War II.[8][10] The AGOT process and its later refinements became standard techniques in the manufacture of nuclear graphite.[11]
The neutron cross section of graphite was investigated during the Second World War in Germany by Walter Bothe, P. Jensen, and Werner Heisenberg. The purest graphite available to them was a product from the Siemens Plania company, which exhibited a neutron absorption cross section of about 6.4 mb[13]: 370 to 7.5 mb.[14] Heisenberg therefore decided that graphite would be unsuitable as a moderator in a reactor design using natural uranium.[3][13][15] Consequently, the German effort to create a chain reaction involved attempts to use heavy water, an expensive and scarce alternative, made all the more difficult to acquire as a consequence of the Norwegian heavy water sabotage by Norwegian and Allied forces. Writing as late as 1947, Heisenberg still did not understand that the only problem with graphite was the boron impurity.[15]
Graphite has also recently been used in nuclear fusion reactors such as the Wendelstein 7-X. As of experiments published in 2019, graphite in elements of the stellarator's wall and a graphite island divertor have greatly improved plasma performance within the device, yielding better control over impurity and heat exhaust, and long high-density discharges.[16]
Wigner effect
[edit]In December 1942 Eugene Wigner suggested[17] that neutron bombardment might introduce dislocations and other damage in the molecular structure of materials such as the graphite moderator in a nuclear reactor. The resulting buildup of energy in the material became a matter of concern[10]: 5 The possibility was suggested that graphite bars might fuse together as chemical bonds at the surface of the bars when opened and closed again. Even the possibility that the graphite parts might very quickly break into small pieces could not be ruled out. However, the first power-producing reactors (X-10 Graphite Reactor and Hanford B Reactor) had to be built without such knowledge. Cyclotrons, which were the only fast neutron sources available, would take several months to produce neutron irradiation equivalent to one day in B Reactor.
This was the starting point for large-scale research programmes to investigate the property changes from fast particle radiation and to predict their influence on the safety and the lifetime of graphite reactors to be built. Influences of fast neutron radiation material properties have been observed many times and in many countries after the first results emerged from the X-10 Graphite Reactor in 1944.
Specific changes to graphite when irradiated include:
- Dimensional change (shrinkage and neutron-induced swelling, as well as possible hardening)
- Change in elastic modulus (measured by impulse excitation technique)
- Change in coefficient of thermal expansion
- Change in thermal conductivity
- Change in electrical resistivity
- Irradiation induced creep
As the state of nuclear graphite in active reactors can only be determined at routine inspections, about every 18 months mathematical modelling of the nuclear graphite as it approaches end-of-life is important. However as only surface features can be inspected and the exact time of changes is not known, reliability modelling is especially difficult.[18] Although catastrophic behaviour such as fusion or crumbling of graphite pieces has never occurred, large changes in many properties do result from fast neutron irradiation which need to be taken into account when graphite components of nuclear reactors are designed. Although not all effects are well understood yet, more than 100 graphite reactors have successfully operated for decades since the 1940s. In the 2010s, the collection of new material property data has improved knowledge significantly. [19][20]
Manufacture
[edit]Reactor-grade graphite must be free of neutron absorbing materials, especially boron, which has a large neutron capture cross section. Boron sources in graphite include the raw materials, the packing materials used in baking the product, and even the choice of soap (for example, borax) used to launder the clothing worn by workers in the machine shop.[11]: 80 Boron concentration in thermally purified graphite (such as AGOT graphite) can be less than 0.4 ppm,[11]: 81 and in chemically purified nuclear graphite it is less than 0.06 ppm.[11]: 47
Nuclear graphite for the UK Magnox reactors was manufactured from petroleum coke mixed with coal-based binder pitch heated and extruded into billets, and then baked at 1,000 °C for several days. To reduce porosity and increase density, the billets were impregnated with coal tar at high temperature and pressure before a final bake at 2,800 °C. Individual billets were then machined into the final required shapes.[21]
Accidents in graphite-moderated reactors
[edit]There have been two major accidents in graphite-moderated reactors, the Windscale fire and the Chernobyl disaster.
In the Windscale fire, an untested annealing process for the graphite was used, causing overheating in unmonitored areas of the core and leading directly to the ignition of the fire. The material that ignited was the canisters of metallic uranium fuel within the reactor. When the fire was extinguished, it was found that the only areas of the graphite moderator to have incurred thermal damage were those that had been close to the burning fuel canisters.[22][23]
In the Chernobyl disaster, the moderator was not responsible for the primary event. Instead, a massive power excursion (exacerbated by the high and positive void coefficient of the RBMK as it was designed and used at the time) during a mishandled test caused the catastrophic failure of the reactor vessel and a near-total loss of coolant supply. The result was that the fuel rods rapidly melted and flowed together while in an extremely high power state, causing a small portion of the core to reach a state of runaway prompt criticality and leading to a massive energy release,[24] resulting in the explosion of the reactor core and the destruction of the reactor building. The massive energy release during the primary event superheated the graphite moderator, and the disruption of the reactor vessel and building allowed the superheated graphite to come into contact with atmospheric oxygen. As a result, the graphite moderator caught fire, sending a plume of highly radioactive fallout into the atmosphere and over a very widespread area.[25]
References
[edit]- ^ Roberts, R. B.; Kuiper, J. B. H. (1939), "Uranium and Atomic Power", Journal of Applied Physics, 10 (9): 612–614, Bibcode:1939JAP....10..612R, doi:10.1063/1.1707351
- ^ "Manhattan Project: The Discovery of Fission, 1938-1939". www.osti.gov. Retrieved 2022-12-01.
- ^ a b c Bethe, Hans (2000), "The German Uranium Project", Physics Today, 53 (7), American Institute of Physics: 34–36, Bibcode:2000PhT....53g..34B, doi:10.1063/1.1292473
- ^ a b Salvetti, Carlo (2001). "Fermi's Pile". In C. Bernardini and L. Bonolis (ed.). Enrico Fermi: His work and legacy. New York N. Y.: Springer Verlag. pp. 177–203. ISBN 3540221417.
- ^ Fermi, Enrico (1946), "Development of the First chain reacting pile", Proceedings of the American Philosophical Society, 90 (1): 2024
- ^ a b c Fermi, Enrico (1965). Collected Papers. Vol. 2. University of Chicago Press.
- ^ Szilard, Gertrude; Weart, Spencer (1978). Leo Szilard: His Version of the Facts. Vol. II. MIT Press. ISBN 0262191687.
- ^ a b c Weinberg, Alvin (1994), "Herbert G. MacPherson", Memorial Tributes, vol. 7, National Academy of Engineering Press, pp. 143–147, doi:10.17226/4779, ISBN 978-0-309-05146-0
- ^ Currie, L. M.; Hamister, V. C.; MacPherson, H. G. (1955). The Production and Properties of Graphite for Reactors. National Carbon Company.
- ^ a b c Eatherly, W. P. (1981), "Nuclear graphite - the first years", Journal of Nuclear Materials, 100 (1–3): 55–63, Bibcode:1981JNuM..100...55E, doi:10.1016/0022-3115(81)90519-5
- ^ a b c d e f Nightingale, R. E. (1962). Nuclear Graphite. Division of Technical Information, United States Atomic Energy Commission. Academic Press. ISBN 0125190506.
- ^ Haag, G. 2005, Properties of ATR-2E Graphite and Property Changes due to Fast Neutron Irradiation, FZ-Juelich, Juel-4813.
- ^ a b Hentschel, Klaus (ed.); Hentschel, Anne M. (translator) (1996), "Document 115", Physics and National Socialism: An Anthology of Primary Sources (English translation of Heisenberg 1947), Birkhäuser, pp. 361–379, ISBN 978-3-0348-0202-4
{{citation}}
:|first1=
has generic name (help) - ^ Haag, 2005.
- ^ a b Heisenberg, Werner (16 August 1947), "Research in Germany on the Technical Applications of Atomic Energy", Nature, 160 (4059): 211–215, Bibcode:1947Natur.160..211H, doi:10.1038/160211a0, PMID 20256200, S2CID 4077785
- ^ Klinger, T.; et al. (2019). "Overview of First Wendelstein 7-X High-Performance Operation". Nuclear Fusion. 59 (11): 112004. Bibcode:2019NucFu..59k2004K. doi:10.1088/1741-4326/ab03a7. hdl:2434/653115.
- ^ Fermi, Enrico (1942), "Report for Month Ending December 15, 1942, Physics Division", United States Atomic Energy Commission report CP-387
- ^ Philip Maul; Peter Robinson; Jenny Burrowand; Alex Bond (June 2017). "Cracking in Nuclear Graphite" (PDF). Mathematics Today. Retrieved 10 March 2019.
- ^ Arregui Mena, J.D.; et al. (2016). "Spatial variability in the mechanical properties of Gilsocarbon" (PDF). Carbon. 110: 497–517. doi:10.1016/j.carbon.2016.09.051. S2CID 137890948.
- ^ Arregui Mena, J.D.; et al. (2018). "Characterisation of the spatial variability of material properties of Gilsocarbon and NBG-18 using random fields" (PDF). Journal of Nuclear Materials. 511: 91–108. Bibcode:2018JNuM..511...91A. doi:10.1016/j.jnucmat.2018.09.008. S2CID 105291655.
- ^ Gareth B. Neighbour (2007). Management of ageing in graphite reactor cores. Royal Society of Chemistry. ISBN 978-0-85404-345-3. Retrieved 2009-06-15.
- ^ "Meeting of RG2 with Windscale Pile 1 Decommissioning Project Team" (PDF). Nuclear Safety Advisory Committee. 2005-09-29. NuSAC(2005)P 18. Retrieved 2008-11-26.
- ^ Marsden, B.J.; Preston, S.D.; Wickham, A.J. (8–10 September 1997). "Evaluation of graphite safety issues for the British production piles at Windscale]". AEA Technology. IAEA. IAEA-TECDOC—1043. Archived from the original on 12 October 2008. Retrieved 13 November 2010.
- ^ Pakhomov, Sergey A.; Dubasov, Yuri V. (2009). "Estimation of Explosion Energy Yield at Chernobyl NPP Accident". Pure and Applied Geophysics. 167 (4–5): 575. Bibcode:2010PApGe.167..575P. doi:10.1007/s00024-009-0029-9.
- ^ "Frequently Asked Chernobyl Questions". International Atomic Energy Agency – Division of Public Information. May 2005. Archived from the original on 23 February 2011. Retrieved 23 March 2011.
External links
[edit]- Manufacturing and Production of Graphite, IAEA Nuclear Graphite Knowledge Base
- Graphite Behaviour under Irradiation, IAEA Nuclear Graphite Knowledge Base